Major Categories of Common Valve Materials (2)
Date:2018-02-03

Chemical Composition
GradeC(Max)Si(Max)Mn(Max)P(Max)S(Max)CrMoNiN(Max)
304L0.030 1.00 2.00 0.045 0.030 18.00/20.00-8.00/13.000.10 
3040.080 1.00 2.00 0.0450.030 18.00/20.00-8.00/11.000.10 











Chemical Properties
GradeYield Strength 
Min (Mpa)
Tensile Strength 
Min (Mpa)
Elongation(%) 
Min
Reduction of Area(%) Min (50mm)Hardness Max
HBHRB
304L1704853050201*92*
3042055153050201*92*
*Maximum hardness not specified in ASTM A182/A182M-13




















Applications
FORGING 
SPECIFICATION
COMMON DESIGNATIONMATERIAL SUFFIXWROUGHT BAR
SPECIFICATION
SERVICE RECOMMENDATIONS(1)COMMON API TRIM#                      FOR BASE MATERIAL
150 TO 600#900 TO 2500#
ASTM A182
F304
18% Chrome; 8% Nickel;
0.08% C Stainless Steel
AS T M A351
Grade CF8
ASTM A479
304
Corrosive or extremely high temperature non-corrosive
services between -450ºF (-268ºC) and +1200ºF
(+649ºC). Above +800ºF (+425ºC) specify carbon content
of 0.04% or greater.
22, 15
ASTM A182
304L
18% Chrome; 8% Nickel;
0.03% C Low Carbon
Stainless Steel
ASTM A 351
Grade CF3
ASTM A479
304L
Brackish water, phosphate solutions, pressurised water
@ 570ºF (299ºC), sea water, steam.
304L+HFS304L+HF
ASTM A182
F304H
18% Chrome; 8% Nickel;
0.08% C Stainless Steel
AST M A351
Grade CF10
ASTM A479
304H
Corrosive or extremely high temperature non-corrosive
services between -450ºF (-268ºC) and +1200ºF
(+649ºC). Above +800ºF (+425ºC) specify carbon content
of 0.04% or greater.
304H+HFS304H+HF

handa valve   High-performance butterfly valve  high pressure   high temperature   zero leakage butterfly valve